Patcham LTD lists 162 grades in Paint & Coatings. The sheets saved on this site are below.
Grades from Patcham LTD
Interior/Exterior Gloss Paint (Formulation #21-10005)
Gradually add Cellulosic Thickener in water and mix at 2.5 ms-1 for 10 minutes. Neutralize to maintain pH 8.5-9. Mix again for 10 minutes at 2.5 ms-1 . Add the raw materials in sequence. Slowly add the pigments and fillers mix thoroughly, continue mixing for 10 minutes at 2 ms-1. Grind at 4 ms-1 until desired Hegman gauge is achieved- 7+ NS/ <10 µm.
Interior/Exterior Matt Paint (Formulation #21-10005)
Gradually add Cellulosic Thickener in water and mix at 2.5 ms-1 for 10 minutes. Neutralize to maintain pH 8.5-9. Mix again for 10 minutes at 2.5 ms-1 . Add the raw materials in sequence. Slowly add the pigments and fillers mix thoroughly, continue mixing for 10 minutes at 2 ms-1. Grind at 4 ms-1 until desired Hegman gauge is achieved. 5+ NS/ min. of 20 µm.
Interior/Exterior Semi Glossy Paint Waterborne Coatings (Formulation #21-10005)
Gradually add Cellulosic Thickener in water and mix at 2.5 ms-1 for 10 minutes. Neutralize to maintain pH 8.5-9. Mix again for 10 minutes at 2.5 ms-1 . Add the raw materials in sequence. Slowly add the pigments and fillers mix thoroughly, continue mixing for 10 minutes at 2 ms-1. Grind at 4 ms-1 until desired Hegman gauge is achieved. -7 NS/ min. of 15 µm.
SB 2K PU Black Topcoat (Formulation #21-20242)
This formulation contains Pat-Add DA 3054, AF 174, LE 1023, and Patcat 3001.
SB 2K PU Clear (Formulation #21-20243)
This formulation contains Pat-Add LE 1777, AF 183, and Patcat 3001.
Solventborne 2K PU White Topcoat (Formulation #21-20001)
This solventborne 2K PU white topcoat features Pat-Add DA 1801. It is suitable for general industrial coatings, wood coatings, and auto refinish coatings.
Talc, Extender Slurries (Formulation #21-10006)
Gradually add cellulosic thickener in water and mix at 2.5 ms-1 for 10 minutes. Neutralize to maintain pH 8.5-9. Mix again for 10 minutes at 2.5 ms-1 . Add the raw materials in sequence. Slowly add the pigments and fillers mix thoroughly, continue mixing 10 minutes at 2 ms-1. Grind the mill base using Glass beads for 2 hours at 21 ms-1 µm / gauge 7+ NS.
Waterborne Epoxy Primer (Formulation #21- 10001)
This waterborne epoxy primer features Pat-Add DA 817. It is suitable for general industrial coatings.
Zinc Oxide, Extender Slurries (Formulation #21-10006)
Gradually add cellulosic thickener in water and mix at 2.5 ms-1 for 10 minutes. Neutralize to maintain pH 8.5-9. Mix again for 10 minutes at 2.5 ms-1 . Add the raw materials in sequence. Slowly add the pigments and fillers mix thoroughly, continue mixing 10 minutes at 2 ms-1. Grind the mill base using Glass beads for 2 hours at 21 ms-1 µm / gauge 7+ NS.
Aluminum Silicate, Extender Slurries (Formulation #21-10006)
Gradually add cellulosic thickener in water and mix at 2.5 ms-1 for 10 minutes. Neutralize to maintain pH 8.5-9. Mix again for 10 minutes at 2.5 ms-1. Add the raw materials in sequence. Slowly add the pigments and fillers mix thoroughly, continue mixing for 10 minutes at 2 ms-1. Grind the mill base using Glass beads for 2 hours at 21 ms-1 µm / gauge 7+ NS.
Calcium Carbonate, Extender Slurries (Formulation #21-10006)
Gradually add cellulosic thickener in water and mix at 2.5 ms-1 for 10 minutes. Neutralize to maintain pH 8.5-9. Mix again for 10 minutes at 2.5 ms-1. Add the raw materials in sequence. Slowly add the pigments and fillers mix thoroughly, continue mixing for 10 minutes at 2 ms-1. Grind the mill base using Glass beads for 2 hours at 21 ms-1 µm/ gauge 7+ NS.
Barium Octoate 12.5%
Barium Octoate 12.5% is a clear liquid for use as a paint drier that is insoluble in water. It is an auxiliary drier that is good at maintaining drying under humid conditions.
Bismuth Octoate 24%
Bismuth Octoate 24% is a clear yellow liquid ideal for use as a paint dryer.
Calcium 10% in BD
Calcium 10% in BD is a clear liquid used as an auxiliary drier. Calcium assists in the through drying process. Improves the action of primary driers.
Calcium Octoate 10%
Calcium Octoate 10% is a clear liquid used as an auxiliary drier. Calcium assists in the through drying process. Improves the action of primary driers.
Calcium Octoate 10% (In D60)
Calcium Octoate 10% (In D60) is a clear liquid used as an auxiliary drier. Calcium assists in the through drying process. Improves the action of primary driers.
Calcium Octoate 4% (Neutral)
Calcium Octoate 4% (Neutral) is a clear liquid used as an auxiliary drier. Calcium assists in the through drying process. Improves the action of primary driers.
Calcium Octoate 5%
Calcium Octoate 5% is a clear liquid used as an auxiliary drier. Calcium assists in the through drying process. Improves the action of primary driers.
Calcium Octoate 5% (Neutral)
Calcium Octoate 5% (Neutral) is a clear liquid used as an auxiliary drier. Calcium assists in the through drying process. Improves the action of primary driers.
Calcium Octoate 6%
Calcium Octoate 6% is a clear liquid used as an auxiliary drier. Calcium assists in the through drying process. Improves the action of primary driers.
Calcium Octoate 8%
Calcium Octoate 8% is a clear liquid used as an auxiliary drier. Calcium assists in the through drying process. Improves the action of primary driers.
Cerium Octoate 12%
Cerium Octoate 12% is a clear yellowish liquid that acts as primary oxidation catalysts and works mainly on the surface of the wet film. It is very weak as an initiator at ambient temperatures and provides some through drying.
Cobalt Neo 10% (In BD)
Cobalt Neo 10% (In BD) is a clear violet liquid that acts as primary oxidation catalysts and works mainly on the surface of the wet film. It is most powerful at ambient temperatures. Can lead to discoloration due to its purple color.
Cobalt Neodecanoate 10%
Cobalt Neodecanoate 10% is a clear blue violet liquid that acts as primary oxidation catalysts and works mainly on the surface of the wet film. It is most powerful at ambient temperatures. Can lead to discoloration due to its purple color.
Cobalt Neodecanoate 12%
Cobalt Neodecanoate 12% is a clear blue violet liquid that acts as primary oxidation catalysts and works mainly on the surface of the wet film. It is most powerful at ambient temperatures. Can lead to discoloration due to its purple color.
Cobalt Octoate 10%
Cobalt Octoate 10% is a clear blue-violet liquid that acts as primary oxidation catalysts and works mainly on the surface of the wet film. It is most powerful at ambient temperatures. Can lead to discoloration due to its purple color.
Cobalt Octoate 10% (In D80)
Cobalt Octoate 10% (In D80) is a clear blue-violet liquid that acts as primary oxidation catalysts and works mainly on the surface of the wet film. It is most powerful at ambient temperatures. Can lead to discoloration due to its purple color.
Cobalt Octoate 12%
Cobalt Octoate 12% is a clear blue-violet liquid that acts as primary oxidation catalysts and works mainly on the surface of the wet film. It is most powerful at ambient temperatures. Can lead to discoloration due to its purple color.
Cobalt Octoate 12% (In D 80)
Cobalt Octoate 12% (In D 80) is a clear blue-violet liquid that acts as primary oxidation catalysts and works mainly on the surface of the wet film. It is most powerful at ambient temperatures. Can lead to discoloration due to its purple color.
Cobalt Octoate 6% (In D80)
Cobalt Octoate 6% (In D80) is a clear blue-violet liquid that acts as primary oxidation catalysts and works mainly on the surface of the wet film. It is most powerful at ambient temperatures. Can lead to discoloration due to its purple color.
Cobalt Octoate 8%
Cobalt Octoate 8% is a clear blue-violet liquid that acts as primary oxidation catalysts and works mainly on the surface of the wet film. It is most powerful at ambient temperatures. Can lead to discoloration due to its purple color.