Bayhydrol® A XP 2695
Covestro (formerly Bayer MaterialScience) 科思创
Bayhydrol® A XP 2695 is an aqueous hydroxyfunctional polyacrylic dispersion that shows a superior chemical resistance, which can be improved by increasing the NCO/OH ratio. This product has an equivalent weight of approx. 830, a flash point (No flash point up to initial boiling point) of > 95, and a density at 20°C of approx. 1.06. This product is mainly for air and forced drying coating systems with a very high chemical resistance. The cured paint films are hard, tough but flexible, glossy and high-bodied with good weather stability, lightfastness and superior chemical resistance. The application of a clearcoat based on Bayhydrol® A XP 2695 directly on wood may lead to discoloration.
Documents
No document is attached to this grade yet.
Availability
Covestro (formerly Bayer MaterialScience) 科思创 publishes documents in the marked regions.
Supplier details
Covestro (formerly Bayer MaterialScience) 科思创 lists this grade in the Chemicals DB directory.
More grades from Covestro (formerly Bayer MaterialScience) 科思创
Also from Covestro (formerly Bayer MaterialScience) 科思创
Baybond® PU 330
Baybond® PU 330 is an anionic, non-ionic polyester urethane polymer, used as the film-forming component in glass fibre sizes. Baybond® PU 330 is commonly used as the film-forming component in glass fiber sizing, especially for glass fibers used to reinforce thermosets. Glass fiber sizes based on Baybond® PU 330 have excellent film-forming properties and adhesion. This product also remains stable when exposed to shear forces. As with any product, use of Baybond® PU 330 in a given application must be tested (including but not limited to field testing) in advance by the user to determine suitability.
Baybond® PU 403
Baybond® PU 403 nionic, non-ionic polyester urethane polymer, used as the filmforming component in glass fibre sizes. It becomes milky white when dispersed in water. This product has a non-volatile content (0.9-1.1g / 1h / 125°C, convection oven) of 39 ± 1, a flow time at 23°C, (4mmcup) of 11-18, and a pH value at 20°C (supply form) of 6.0-8.0.
Baybond® PU 405
Baybond® PU 405 is an anionic/non-ionic crosslinking polyether urethane polymer used as the film-forming component in glass fibre sizes. This product becomes milky white when dispersed in water. This product has a non-volatile content (0.9-1.1g / 1h / 125°C, convection oven) of 32-35, a flow time at 23°C, (4mmcup) of 11-18, and a pH value 20°C (supply form) of 6.0-8.0. Baybond® PU 405 was developed for the sizing of glass fibres used to reinforce thermoplastics, particularly polyamide. Glass fibre sizes based on Baybond® PU 405 are characterised by their outstanding film-forming properties and very good adhesion. They have very good colourfastness, even at high temperatures. The mechanical film properties of the product are developed fully by post-crosslinking at temperatures from 170°C for a duration of 20 minutes. Baybond® PU 405 is also highly resistant to shear forces and hydrolysis.
Baybond® PU 406
Baybond® PU 406 is a non-ionic polyurethane polymer used as the film-forming component in glass fiber sizes. This product displays a milky white dispersion in water. It has a non-volatile content (0.9-1.1g / 1h / 125°C, convection oven) of 34.5 ± 1.5, a flow time at 23°C, (4mmcup) of 10-22, and a pH value at 20°C, (supply form) of 5.5-7.5.